Method of making radiographically opaque plastic tubing

ABSTRACT

A method of making flexible radiographically opaque plastic tubing for use as an X-ray catheter. The tubing is transparent to visible light and is rendered X-ray opaque by the incorporation of a diol of tetrabromophthalic anhydride. The radiographically opaque properties enable the tubing to be used as a catheter whose position within the body cavity can be determined by X-ray observation.

United States Patent Slingluff et al.

METHOD OF MAKING RADIOGRAPHICALLY OPAQUE PLASTIC TUBING Inventors: Eugene L. Slingluff, East Troy,

Eli Ostoich, Milwaukee, both of Wis.

Sunlite Plastics, Inc., Milwaukee, Wis.

Filed: July 19, 1973 Appl. No.: 380,727

Related US. Application Data Division of Ser. No. 222,983, Feb. 2, 1972, Pat. No. 3,749,134.

Assignee:

US. Cl. 252/478 Int. Cl. G2lf l/l0 Field of Search 250/519; 252/300, 478;

[56] References Cited UNITED STATES PATENTS 2,247,880 7/1941 Guerbet 252/478 3,361,700 l/l968 Archer et a] 252/478 Primary Examiner-Stephen C. Bentley Attorney, Agent, or FirmAndrus, Sceales, Starke & Sawall [57] ABSTRACT A method of making flexible radiographically opaque plastic tubing for use as an X-ray catheter. The tubing is transparent to visible light and is rendered X-ray opaque by the incorporation of a die] of tetrabromophthalic anhydride. The radiographically opaque properties enable the tubing to be used as a catheter whose position within the body cavity can be determined by X-ray observation.

4 Claims, No Drawings METHOD OF MAKING RADIOGRAPHICALLY OPAQUE PLASTIC TUBING This is a division of application Ser. No. 222,983, filed Feb. 2, 1972, now U.S. Pat. No. 3,749,134.

BACKGROUND OF THE INVENTION to X-rays, and through X-ray observation the position of the catheter within the body cavity can be determined.

In the past, a number of different types of X-ray opaque catheters have been proposed. Attempts have been made to develop an X-ray opaque catheter by applying or painting X-ray opaque substances on the outer surface of the catheter. However, X-ray opaque markings of this type are often destroyed or rendered relatively ineffective through cleaning or sterilization of the catheter. Furthermore, many X-ray opaque substances camnot be used as an external coating due to their toxicity to body tissue.

In other cases an X-ray opaque material has been incorporated within the plastic tubing to thereby render the entire wall of the tubing X-ray opaque. In most instances, however, the resulting catheters have been opaque not only to X-rays, but also to visible light. If the plastic tubing is opaque to visible light, substances flowing through the tubing cannot be visually observed which is a decided disadvantage.

In order to overcome the inherent disadvantages of a catheter which is opaque to visible light, it has also been proposed to incorporate a narrow strip of X-ray opaque material within the wall of the catheter so that the major portion of the catheter wall would be transparent to visible light. This procedure not only increases the cost of fabrication, but reduces the width of the X-ray opaque substance, and when dealing with catheters of small diameter, the narrow X-ray opaque strip is difficult to observe by fluoroscope or X-ray film.

SUMMARY OF THE INVENTION The invention relates to a method of making flexible plastic tube to be used as an X-ray catheter which is transparent to visible light and yet is radiographically opaque. The tubing is fabricated of a thermoplastic resin containing one or more plasticizers to provide the desired hardness and is rendered radiographically opaque by the incorporation of a diol of tetrabromophthalic anhydride.

As the tubing is X-ray opaque, its position within the body cavity can be readily determined by X-ray observation or fluoroscope. While radiographically opaque, the tubing is clear or transparent to visible light so that substances flowing through the tubing can be readily observed.

The diol can be distributed throughout the entire wall of the tubing, thereby rendering the entire tube radiographically opaque, or alternately, the diol can be incorporated in certain areas or zones of the tubing to form a longitudinally extending strip, or other desired patterns.

The use of the diol to provide the X-ray opaque characteristics eliminates the need for conventional X-ray opaque compounds, such as bismuth salts or iodine compounds, which in some cases cannot be tolerated by the body tissue.

DESCRIPTION OF THE PREFERRED EMBODIMENT The plastic tubing produced by the method of the invention is a flexible non-absorptive, non-toxic material formed of a thermoplastic resin, one or more plasticizers, and a small amount of a diol of tetrabromophthalic anhydride having the following formula:

C0 CH CH OCH CH OH CO2CH2-CHOH Br I CH3 Br The diol is a substantially colorless liquid having a hydroxyl number of 162, an equivalent weight of 346, an acid number of 0.63 and contains 45.5% bromine.

The particular thermoplastic resin to be employed in the tubing is not critical to the invention and anyv of the common thermoplastic resins can be utilized, such as polyethylene, vinyl polymers such as vinylchloride polymers or copolymers with other vinyl esters such as vinyl acetate, vinylidene chloride polymers, flexible forms of nylon, flexible polyurethane, and the like.

It is preferred that the plastic material be unpigmented so that it is transparent to visible light, making it possible to see the flow of substances within the tubing. However, it is possible to include a small amount of pigment in the resin formulation to provide a tint to the tubing while still maintaining the transparent characteristics.

The specific plasticizer to be employed in the composition is not critical to the invention and any of the conventional plasticizers commonly used in formulating thermoplastic compositions can be utilized, such as di( 2-ethyhexyl) phthalate, dioctyl phthalate, diisooctyl phthalate, diethyl phthalate, dioctyl adipate, diphenyl 2-ethyl hexyl phosphate, ethyl phthalyl ethyl glycolate,

butyl phthalhyl butyl glycolate, butyl benzyl phthalate, and the like.

The amount of plasticizer depends on the desired hardness or rigidity in the tubing, and if the tubing is to be employed as a catheter, it is desired that the tubing be relatively soft and flexible. In general, the more flexible types of tubing will have a Shore A durometer hardness of 45 to 90, while more rigid types of the plastic tubing may have a Shore D durometer hardness of 77 to 83. In general, the plasticizer us used in an amount of 5 to by weight of the thermoplastic resin.

The diol provides radiographically opaque properties for the thermoplastic composition, and yet due to the fact that it is colorless will not render the plastic composition opaque to visible light.

It is preferred to blend the diol in with the thermoplastic composition and thereafter extrude the composition in the form of tubing so that the tetrabromophthalic anhydride is distributed throughout the entire tubing wall. However, in certain instances the diol can be incorporated only in portions of the wall of the tubing, as for example, as a longitudinal stripe which extends the length of the tubing, or the diol can be incorporated in any other desired pattern along the length of the tubing. In either case the portion of the tubing which contains the diol will be opaque to X-rays so that it can be readily seen by X-ray observation when in the body cavity.

The thermoplastic composition containing the diol can be perepared by conventional procedures. In general, the plasticizers and the diol are blended into the resin and generally a small amount of powdered lubri cant such as zinc stearate is also incorporated. The thoroughly blended mixture is then extruded in the form of tubing by conventional extrusion equipment.

The amount of the diol to be incorporated in the thermoplastic composition can vary withinwide limits depending on the degree of radiographic opacity required and also depending on the wall thickness of the tubing. ln general, the diol can be employed in the amount of 5 to 70% by weight of the thermoplastic resin composition (including the resin and plasticizers) and preferably in the amount of to 40% by weight of the thermoplastic resin composition. For tubing of thicker wall section, a lesser proportion of the diol is required because of the increased concentration of the material in the thicker wall.

The following examples illustrate the manner of preparing the X-ray opaque tubing of the invention:

EXAMPLE NO. I

100 parts by weight of polyvinyl chloride were blended with 44 parts of di( 2-ethylhexyl)phthalate, parts of epoxidized linseed oil, and 12 parts of the previously identified diol of tetrabromophthalic anhydride. In addition, 0.08 gr. of violet pigment was added to the mixture to provide a bluish cast, and 2 oz. of zinc stearate was incorporated as a lubricant.

The resulting blend was extruded from a standard extrusion machine having a machine body temperature of 325F. The extruded tubing had an ID of 0.200 inch and an OD of 0.360 inch, and a Shore A durometer hardness of 78. The tubing had a faint blue cast, was transparent to visible light, but radiographically opaque.

EXAMPLE NO. ll

100 parts by weight of polyvinyl chloride were blended with 44 parts of di( 2-ethylhexyl)phthalate, 2O

parts of epoxidized linseed oil, and 24 parts of the previously identified diol of tetrabromophthalic anhydride. In addition, 2 oz. of zinc stearate was incorporated as a lubricant.

The resulting blend was extruded from a standard extrusion machine having a machine body temperature of 325F. The extruded tubing had an ID of 0.060 inch and an OD of 0.092 inch, and A Shore A'durometer hardness of 78. The tubing was clear and transparent to visible light, but radiographically opaque.

Various modes of carrying out the invention are contemplated as being within the scope of the following claims particularly pointing out and distinctly claiming the subject matter which is regarded as the invention,

We claim:

1. A method of rendering a thermoplastic composition radiographically opaque, comprising the step of incorporating with the thermoplastic composition a material having the following formula:

CO CH CH OCH CH OH Br CO CH- ,CH--OH 2. The method of claim 1, wherein said material is incorporated in an amount of 15 to 40% by weight of said composition.

3. The method of claim 1, and including the step of mixing a plasticizer with said thermoplastic composition prior to incorporating said material, said plasticizer comprising from 5 to by weight of said thermoplastic composition. I

4. A method of making radiographically opaque plastic tubing, comprising the steps of incorporating with a thermoplastic composition a compound having the following formula:

co H C CH OCH CH OH Br CO CH CIHOH CH Br and extruding the thermoplastic composition after incorporation of said material into tubular shape. 

1. A METHOD OF RENDERING A THERMOPLASTIC COMPOSITION RADIOGRAPHICALLY OPAQUE, COMPRISING THE STEP OF INCORPORATING WITH THE THERMOPLASTIC COMPOSITION A MATERIAL HAVING THE FOLLOWING FORMULA:
 2. The method of claim 1, wherein said material is incorporated in an amount of 15 to 40% by weight of said composition.
 3. The method of claim 1, and including the step of mixing a plasticizer with said thermoplastic composition prior to incorporating said material, said plasticizer comprising from 5 to 100% by weight of said thermoplastic composition.
 4. A method of making radiographically opaque plastic tubing, comprising the steps of incorporating with a thermoplastic composition a compound having the following formula: 